- TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness,
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness,
| Category | Metal , Nonferrous Metal , Titanium Alloy , Alpha/Beta Titanium Alloy |
| Manufacturer | TIMET |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness,.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod or Thickness,
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.42 g/cc | 0.160 lb/in³ | Typical |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | >= 895 MPa | >= 130000 psi | Longitudinal |
| Tensile Strength, Yield | >= 828 MPa @Strain 0.200 % |
>= 120000 psi @Strain 0.200 % |
Longitudinal |
| Elongation at Break | >= 10 % | >= 10 % | Longitudinal |
| Reduction of Area | >= 25 % | >= 25 % | Longitudinal |
| Modulus of Elasticity | 105 - 120 GPa | 15200 - 17400 ksi | Typical |
| Poissons Ratio | 0.31 | 0.31 | |
| Shear Modulus | 41.0 - 45.0 GPa | 5950 - 6530 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| 9.40 µm/m-°C @Temperature 20.0 - 425 °C |
5.22 µin/in-°F @Temperature 68.0 - 797 °F |
||
| 9.70 µm/m-°C @Temperature 20.0 - 650 °C |
5.39 µin/in-°F @Temperature 68.0 - 1200 °F |
||
| Specific Heat Capacity | 0.586 J/g-°C | 0.140 BTU/lb-°F | |
| Thermal Conductivity | 6.60 W/m-K | 45.8 BTU-in/hr-ft²-°F | |
| Melting Point | 1674 °C | 3045 °F | |
| Liquidus | >= 1636 °C | >= 2977 °F | |
| Maximum Service Temperature, Air | 350 °C | 662 °F | Reasonable mechanical properties retained |
| Beta Transus | 995 °C | 1820 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 5.5 - 6.75 % | 5.5 - 6.75 % | |
| Carbon, C | <= 0.080 % | <= 0.080 % | |
| Hydrogen, H | <= 0.015 % | <= 0.015 % | |
| Iron, Fe | <= 0.40 % | <= 0.40 % | |
| Nitrogen, N | <= 0.050 % | <= 0.050 % | |
| Oxygen, O | <= 0.20 % | <= 0.20 % | |
| Titanium, Ti | 87.6 - 91 % | 87.6 - 91 % | Calculated as remainder |
| Vanadium, V | 3.5 - 4.5 % | 3.5 - 4.5 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000168 ohm-cm | 0.000168 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 20 oersteds |
Users viewing this material also viewed the following:
- Overview of materials for Polyester Thermoplastic Elastomer
- Lubrizol Advanced Materials PEARLTHANE® 11H94 Thermoplastic Polyurethane Elastomer
- Lanxess Pocan® DP C 1502 000000 PBT + PC
- Ter Hell Plastic Terez® PA 6 7500 TF 20 GF 20 Polyamide 6, 20% PTFE chemically bonded 20% glass fiber reinforced
- Asahi Kasei ASACLEAN SX Purging Compound
- Bulk Molding Compounds BMC 620X Mineral Filled, Glass Fiber Reinforced Polyester Compound
Copyright © lookpolymers.com All Rights Reserved