Materion Beryllium Copper Alloy 174 Strip; 1/2HT (TH02) Temper (UNS C17410)
| Category | Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy |
| Manufacturer | Materion Corporation (former Brush Wellman) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Materion Beryllium Copper Alloy 174 Strip; 1/2HT (TH02) Temper (UNS C17410).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 95%Stress Relaxation after 1000 hrs @ 200°C: 67%Formability Ratio, 90° Bend, Radius/Thickness (Good Way): 0.5Formability Ratio (bad Way): 0.5Superficial Hardness: 30T 75.5-81.9Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.80 g/cc | 0.318 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 89 - 98 | 89 - 98 | |
| Hardness, Vickers | 180 - 230 | 180 - 230 | |
| Tensile Strength, Ultimate | 655 - 790 MPa | 95000 - 115000 psi | |
| Tensile Strength, Yield | 550 - 690 MPa | 79800 - 100000 psi | |
| Elongation at Break | 10 - 20 % | 10 - 20 % | |
| Modulus of Elasticity | 138 GPa | 20000 ksi | |
| Fatigue Strength | 280 - 310 MPa @# of Cycles 1.00e+8 |
40600 - 45000 psi @# of Cycles 1.00e+8 |
Reverse Bending (R=1) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 200 °C |
10.0 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Thermal Conductivity | 230 W/m-K | 1600 BTU-in/hr-ft²-°F | |
| Melting Point | 1030 - 1070 °C | 1890 - 1960 °F | |
| Solidus | 1030 °C | 1890 °F | |
| Liquidus | 1070 °C | 1960 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Beryllium, Be | 0.15 - 0.50 % | 0.15 - 0.50 % | |
| Cobalt, Co | 0.35 - 0.60 % | 0.35 - 0.60 % | |
| Copper, Cu | 99 % | 99 % | as balance |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000290 - 0.00000380 ohm-cm | 0.00000290 - 0.00000380 ohm-cm | 45-60% IACS Conductivity |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1444 PC Copolymer
- Haysite H900 Polyester, Glass Reinforced
- Silberline Silvet® 330-20-E
- Teknor Apex Laripur® LPR 9060HFM Thermoplastic Polyurethane
- A. Schulman PP 1102-01 Polypropylene General Purpose, Molding Grade Polypropylene
- Ensinger Tecatron® XP-64B Compression Molded PPS Compound, 40% Fiberglass, Black Pigmented
- 3M AC-215 Class B-1/2 Aerospace Sealant
- Henkel Turco D HX-357 Make-Up and Replenisher Deoxidizer
- BASF Neopolen® P 9435 0.035 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved