SABIC Innovative Plastics Cycoloy® FXC630FE PC+ABS (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycoloy®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycoloy® FXC630FE PC+ABS (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Multi purpose flame retarded PC+ABS injection moulding grade, suitable for those applications that require ferrite colour effects.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.60 % @Temperature 23.0 °C	0.60 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	on tensile bar; SABIC Method
Melt Flow	13 g/10 min @Load 2.16 kg, Temperature 260 °C	13 g/10 min @Load 4.76 lb, Temperature 500 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	122	122	ISO 2039-2
Hardness, H358/30	116 MPa	16800 psi	ISO 2039-1
Tensile Strength at Break	40.0 MPa	5800 psi	5 mm/min; ISO 527
Tensile Strength, Yield	50.0 MPa	7250 psi	5 mm/min; ISO 527
Elongation at Yield	4.0 %	4.0 %	5 mm/min; ISO 527
Tensile Modulus	2.80 GPa	406 ksi	1 mm/min; ISO 527
Flexural Yield Strength	98.0 MPa	14200 psi	2 mm/min; ISO 178
Flexural Modulus	2.80 GPa	406 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	5.00 kJ/m² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	80103; ISO 180/1A
	8.00 kJ/m² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	80103; ISO 180/1A
Charpy Impact, Notched	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA
	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles	82 @Load 1.00 kg	82 @Load 2.20 lb	CS-17; SABIC Method

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	75.0 µm/m-°C @Temperature -40.0 - 40.0 °C	41.7 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	75.0 µm/m-°C @Temperature -40.0 - 40.0 °C	41.7 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Thermal Conductivity	0.200 W/m-K	1.39 BTU-in/hr-ft²-°F	ISO 8302
Hot Ball Pressure Test	<= 85.0 °C	<= 185 °F	IEC 60695-10-2
Vicat Softening Point	94.0 °C	201 °F	Rate B/50; ISO 306
	97.0 °C	207 °F	Rate B/120; ISO 306
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL 94 by SABIC-IP
Oxygen Index	32 %	32 %	LOI; ISO 4589
Glow Wire Test	960 °C @Thickness 3.20 mm	1760 °F @Thickness 0.126 in	Glow Wire Flammability Index; IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	ROA; IEC 60093
Dielectric Constant	2.7 @Frequency 1.00e+6 Hz	2.7 @Frequency 1.00e+6 Hz	IEC 60250
	2.8 @Frequency 50.0 - 60.0 Hz	2.8 @Frequency 50.0 - 60.0 Hz	IEC 60250
Dielectric Strength	17.0 kV/mm @Thickness 3.20 mm	432 kV/in @Thickness 0.126 in	in oil; IEC 60243-1
	25.0 kV/mm @Thickness 1.60 mm	635 kV/in @Thickness 0.0630 in	in oil; IEC 60243-1
	35.0 kV/mm @Thickness 0.800 mm	889 kV/in @Thickness 0.0315 in	in oil; IEC 60243-1
Dissipation Factor	0.0040 @Frequency 50.0 - 60.0 Hz	0.0040 @Frequency 50.0 - 60.0 Hz	IEC 60250
	0.0080 @Frequency 1.00e+6 Hz	0.0080 @Frequency 1.00e+6 Hz	IEC 60250

Descriptive Properties	Value	Comments
Ball Pressure Test, 75°C +/- 2°C	PASSES	IEC 60695-10-2