LTL Color Compounds Surlyn Reflection Series® SURSG201UG Surlyn Resin/Nylon 6 Alloy
| Category | Polymer , Thermoplastic , Ionomer , Nylon , Nylon 6 |
| Manufacturer | LTL Color Compounds |
| Trade Name | Surlyn Reflection Series® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds Surlyn Reflection Series® SURSG201UG Surlyn Resin/Nylon 6 Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A patented alloy of DuPont™ Surlyn® resin and nylon 6 for applications that require a high gloss, molded in color surface finish directly from the mold.All information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.043 g/cc | 1.043 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | 0.125; ASTM D955 |
| Melt Flow | 2.0 - 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 - 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.4 MPa | 5710 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 40.3 MPa | 5850 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 220 % | 220 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 11 % | 11 % | 2.0 in/min; ASTM D638 |
| Flexural Modulus | 1.14 GPa | 165 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm @Temperature -30.0 °C |
5.00 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 57.8 °C | 136 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 241 °C | 465 °F | 0.5 |
| Middle Barrel Temperature | 241 °C | 465 °F | 0.5 |
| Front Barrel Temperature | 241 °C | 465 °F | 0.5 |
| Melt Temperature | 232 - 257 °C | 450 - 495 °F | |
| Mold Temperature | 51.7 - 57.2 °C | 125 - 135 °F | |
| Drying Temperature | 60.0 - 62.8 °C | 140 - 145 °F | |
| Dry Time | 6 - 8 hour | 6 - 8 hour | nominal; maximum drying time of 24 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 70 % | 30 - 70 % | 50% optimum |
| Vent Depth | 0.00254 - 0.00381 cm | 0.00100 - 0.00150 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP Lubricomp DFL329EF PC
- Nilit FRIANYL B63 HH-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced
- LyondellBasell Pro-fax 6523 Polypropylene Homopolymer, General Purpose
- DuPont Elvanol® 70-03 Polyvinyl Alcohol Fully Hydrolyzed General Purpose Grade
- Eurostar Starflam AFR470X2 PA66, 35% Glass Filled, Injection Molded
- Alliance Polymers Viprene™ G65A-32U-BLK Thermoplastic Vulcanizate Elastomer
- Asahi Glass Fluon® PTFE
- Aremco Pyro-Tape™ 682-HR High Temperature Tape Bi-layer aluminum/fiberglass with silicone adhesive
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.5 PHR Sulfur
- Addiplast Addinyl C2 V15 Nylon 66/6, 15% Glass Filled
Copyright © lookpolymers.com All Rights Reserved