SABIC Innovative Plastics Cycoloy® CY203 PC+ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® CY203 PC+ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Cycoloy* CY203 is a industrial quality PC+ABS flame retardant grade for injection moulding applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Melt Index of Compound | 15 g/10 min @Load 2.16 kg, Temperature 260 °C |
15 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 95.0 °C | 203 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
IEC 60695-2-12 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- BP Amoco Amoco® 7644 Polypropylene Homopolymer (discontinued **)
- LyondellBasell Petrothene® NA247000 Low Density Polyethylene, Injection Molding Grade
- Schott N-BALF5 Glass
- SABIC Innovative Plastics Noryl GTX GTX979 PPE+PA (Europe-Africa-Middle East)
- Bapolan® PS6078-G Polystyrene Compound
- 3M Safety-Walk™ 220 Clear Slip-Resistant Fine Resilient Tapes and Treads
- 3M 12036 Black 3/16" (4.8 mm) Polyurethane Foam
- Adell AR-17 Nylon 66, 35% Glass Reinforced
- Advanced Polymer Alloys DuraGrip™ 6870 Thermoplastic Elastomer
- Polyram Polytron A50B01 Nylon 6.6, 50% Long Fiber Glass
Copyright © lookpolymers.com All Rights Reserved