SABIC Innovative Plastics Cycoloy® C2950HF PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C2950HF PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced impact and heat properties plus improved flow for various applications.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption at Equilibrium 0.40 %
0.40 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 22 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 22 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength, Yield 64.0 MPa
9280 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 40 %
40 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 96.0 MPa
13900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 2.58 GPa
374 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 4.53 J/cm
8.49 ft-lb/in
ASTM D256
Dart Drop, Total Energy 54.0 J
39.8 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 40.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 40.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 101 °C

@Thickness 6.40 mm
 214 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C

@Thickness 3.20 mm
 189 °F

@Thickness 0.126 in
 unannealed; ASTM D648
93.0 °C

@Thickness 6.40 mm
 199 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 112 °C
234 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical without Impact 85.0 °C
185 °F
UL 746B
Flammability, UL94 V-2

@Thickness 0.760 mm
 V-2

@Thickness 0.0299 in
 UL 94
V-0

@Thickness 1.49 mm
 V-0

@Thickness 0.0587 in
 UL 94
5VB

@Thickness 2.48 mm
 5VB

@Thickness 0.0976 in
 UL 94
5VA

@Thickness 3.40 mm
 5VA

@Thickness 0.134 in
 UL 94
Oxygen Index 30 %
30 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.60e+17 ohm-cm
1.60e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ASTM D257
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
 2.7

@Frequency 1.00e+6 Hz
 ASTM D150
2.8

@Frequency 50.0 - 60.0 Hz
 2.8

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Dielectric Strength 24.3 kV/mm

@Thickness 3.20 mm
 617 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
Dissipation Factor 0.0052

@Frequency 50.0 - 60.0 Hz
 0.0052

@Frequency 50.0 - 60.0 Hz
 ASTM D150
0.0071

@Frequency 1.00e+6 Hz
 0.0071

@Frequency 1.00e+6 Hz
 ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A