SABIC Innovative Plastics Cycoloy® C2950 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® C2950 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| 1.22 g/cc | 1.22 g/cc | color; ASTM D792 | |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 260 °C |
10 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 102 MPa | 14800 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.65 GPa | 384 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| 1.60 J/cm @Temperature -30.0 °C |
3.00 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 54.0 J @Temperature -30.0 °C |
39.8 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| 61.0 J @Temperature 23.0 °C |
45.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C @Thickness 6.40 mm |
219 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 3.20 mm |
194 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 112 °C | 234 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 85.0 °C | 185 °F | UL 746B |
| UL RTI, Mechanical with Impact | 85.0 °C | 185 °F | UL 746B |
| UL RTI, Mechanical without Impact | 85.0 °C | 185 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.49 mm |
V-0 @Thickness 0.0587 in |
UL 94 |
| 5VB @Thickness 2.48 mm |
5VB @Thickness 0.0976 in |
UL 94 | |
| Oxygen Index | 32 % | 32 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 50.0 - 60.0 Hz |
3.0 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
ASTM D150 | |
| Dielectric Strength | 19.4 kV/mm @Thickness 3.20 mm |
493 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0049 @Frequency 100 Hz |
0.0049 @Frequency 100 Hz |
ASTM D150 |
| 0.0050 @Frequency 50.0 - 60.0 Hz |
0.0050 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Users viewing this material also viewed the following:
- Radici Radilon® A ECP3808 (cond.) Nylon 66
- Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F)
- SABIC Innovative Plastics LNP Stat-kon DE002E PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP Stat-kon EE002ER PEI (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene
- DuPont Surlyn® 1650SB
- Tra-Con Tra-Duct 921U02 Long Pot Life Silver-Filled Epoxy
- CP-Polymer-Technik Wellamid® 6000/58 CP Nylon 6, Impact Modified Until -40°C, Conditioned
- DuPont Performance Polymers Hypalon® CP-337 Adhesion Primer, General Description (discontinued **)
- Special Metals INCOLOY® Alloy 020
Copyright © lookpolymers.com All Rights Reserved