SABIC Innovative Plastics Cycolac® MG94 ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® MG94 ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Superior flow, injection molding ABS. Good impact. For thin-wall applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Viscosity | 172000 cP | 172000 cP | Melt Viscosity, 240°C, 1000 sec-1; ASTM D3825 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 11.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
11.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 12 g/10 min @Load 5.00 kg, Temperature 220 °C |
12 g/10 min @Load 11.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 18 % | 18 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 79.0 MPa | 11500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 21.0 J @Temperature 23.0 °C |
15.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 88.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 84.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 98.0 °C | 208 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.52 mm |
HB @Thickness 0.0598 in |
UL 94 |
Users viewing this material also viewed the following:
- Mitsui AURUM® JGN3030 Thermoplastic Polyimide Resin, Amorphous (discontinued **)
- Momentive Performance Materials RTV5229 Neutral Cure, One Component RTV Adhesive Sealant
- Mueller Ecostreamâ„¢ C36300 Copper Zinc Lead Alloy
- Stir SpA C 2053 60 AT (PVC)
- Silikony Polskie Polastosil M-56 Silicone Rubber
- A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound
- Asahi Kasei Tenac® 5010 Homopolymer Acetal Resin
- 3M 9627 Adhesive Transfer Tape with Quick Bonding Adhesive 360
- BASF 2,4-Ethylmethylimidazole S
Copyright © lookpolymers.com All Rights Reserved