BASF Ultramid® 7523-2AM BK ND3007 33% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 7523-2AM BK ND3007 33% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 7523-2AM BK ND3007 is an impact modified, 33% glass reinforced, heat stabilized injection molding PA6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | 5mm/min; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | 5mm/min; ISO 527 |
| 7.0 % | 7.0 % | 0.2 in/min; ASTM Test | |
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 6.62 GPa | 960 ksi | ASTM Test |
| 8.50 GPa | 1230 ksi | ISO Data | |
| Izod Impact, Notched | 1.71 J/cm @Thickness 3.17 mm |
3.20 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO Test |
| Charpy Impact, Notched | 2.10 J/cm² | 9.99 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 249 °C | 480 °F | ASTM Test |
| 260 °C | 500 °F | ISO 75 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM Test |
| 245 °C | 473 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Commercial Status | Active America | |
| Impact Modified | Yes | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Ineos ABS Lustran® Guardian™ 682 ABS, Injection Molding Grade
- Materion Beryllium Copper Alloy M25 Wire; A (TB00) Temper; 1.3-12.7 mm Diameter (UNS C17300)
- Gouda Vuurvast VIBRON 180 T Dense Vibrating Refractory Castable
- Solvay Specialty Polymers Solef® 1006 Polyvinylidene Fluoride (PVDF)
- Spartech Tuf-Glas Impact Modified Acrylic Sign Grade Sheet
- Techmer ES HiFill® PA6/6 GF50 HS L BK 50% Glass Filled (Dry)
- DuPont Performance Polymers Zytel® HTN FR55G50NHLW BK046 Polyphthalamide (PPA) (Unverified Data**)
- ExxonMobil 447 Mobilmet 440 Series
- Bisalloy Steels BisPlate 80 Thickness >80-100 mm
Copyright © lookpolymers.com All Rights Reserved