SABIC Innovative Plastics Cycolac® MG38N ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® MG38N ABS.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Very high impact ABS. Toughness/rigidity. Good fatigue resistance. NSF Standard 61 certified in limited colors (restrictions may apply)>
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Viscosity 245000 cP
245000 cP
Melt Viscosity, 240°C, 1000 sec-1; ASTM D3825
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 3.7 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 3.7 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
15 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 15 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 34.0 MPa
4930 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 45.0 MPa
6530 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 26 %
26 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.1 %
2.1 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.27 GPa
329 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 72.0 MPa
10400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 3.74 J/cm
7.01 ft-lb/in
ASTM D256
Dart Drop, Total Energy 31.0 J

@Temperature 23.0 °C
 22.9 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 88.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 49.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 86.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C

@Thickness 3.20 mm
 203 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C

@Thickness 3.20 mm
 176 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 99.0 °C
210 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.52 mm
 HB

@Thickness 0.0598 in
 UL 94
Electrical Properties Metric English Comments
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index >= 600 V
>= 600 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746A