- Thermoplastic
- Polypropylene (PP)
- Polypropylene with 10% Talc Filler
- RheTech Products T10P100-00 10% Talc Reinforced Polypropylene, Natural
RheTech Products T10P100-00 10% Talc Reinforced Polypropylene, Natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products T10P100-00 10% Talc Reinforced Polypropylene, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Consumer goodsIP structural componentsInterior trimInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 10 % | 10 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 230 °C |
22 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength at Break | 33.1 MPa | 4800 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.93 GPa | 280 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Temperature 23.0 °C |
0.500 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.904 J | 0.667 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Middle Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Front Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Nozzle Temperature | 210 - 221 °C | 410 - 430 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 55.2 - 103 MPa | 8000 - 15000 psi | |
| Hold Pressure | 27.6 - 51.7 MPa | 4000 - 7500 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- MV Labs TB500 TbF3 Terbium fluoride
- Radici Heraflex® HA 60-22-60 TPS-SEBS Thermoplastic Elastomer
- North Wood Plastics 60 HDPE + UNIFILL (20% Wood Fiber)
- Magyar Aluminum ALO-P54-04 Alumina
- A. Schulman PP 1452 Polypropylene Medium Impact Polypropylene
- Dow Corning FOX® PMCP22 Flowable Oxide
- Chi Mei Kibiton® PB-5903 SBC
- Arlon R33670N004 0.004" (0.102 mm) Uncured Silicone Rubber with K2030 PEN Film Substrate
- Techmer ES Plaslube® NY-1/SI/5 NAT PA66
- Solvay MACKAM® OSF-60 Surfactant
Copyright © lookpolymers.com All Rights Reserved