BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3ZG3 is an impact-modified, 15% glass fiber reinforced injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | dry; ISO 1183 |
| Water Absorption | 7.5 % | 7.5 % | beginning dry; ISO 62 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD |
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 275 °C |
30 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 127 MPa @Temperature -40.0 °C |
18400 psi @Temperature -40.0 °F |
ISO Data |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | 5mm/min; ISO 527 |
| Elongation at Break | 18 % | 18 % | 5mm/min; ISO 527 |
| 5.2 % @Temperature -40.0 °C |
5.2 % @Temperature -40.0 °F |
ISO Data | |
| Tensile Modulus | 2.90 GPa | 421 ksi | 1mm/min; ISO 527 |
| Charpy Impact Unnotched | 11.0 J/cm² | 52.4 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| 220 °C | 428 °F | ASTM Test |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.2 @Frequency 1.00e+6 Hz |
6.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz |
0.20 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Form | Pellets | |
| Impact Modified | Yes | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible XV3440 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polymer Resources PC/ABS-G30 General Purpose PC/ABS Alloy, 30% Glass Filled
- NOVA Chemicals Novapol® LF-0218-AB LDPE Film Resin (discontinued **)
- Schott G018-159 Dental Glass
- Silberline Aquasil® "BP" 5745
- Borealis CA9150 Low Density Polyethylene
- Arlon Thermabond® 99950N008 Silicone Rubber/Fiberglass Laminate
- Austin Novel Materials Texalan® 490A Polyester-based TPU
- 3M Scotchkote™ 75RG 530 Urethane Elastomer
Copyright © lookpolymers.com All Rights Reserved