NOVA Chemicals Sclair® 8107G UV8D Butene LLDPE Rotational Molding Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded
Manufacturer NOVA Chemicals
Trade Name Sclair®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® 8107G UV8D Butene LLDPE Rotational Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent ESCR, Excellent low temperature impact properties, Excellent low shrinkage and warpage properties, Very good processability, UL 94-HB listedApplications: Food and laundry materials handling, IBCs, Chemical containers, Parts requiring flat surfaces or low shrinkage characteristics, Intricate custom partsAdditives: Processing antioxidants, UV stabilizersInformation provided by NOVA Chemicals.
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ASTM D792
ESCR 100% Igepal® >= 1000 hour

@Temperature 50.0 °C
>= 1000 hour

@Temperature 122 °F
F<sub>50</sub>; Condition A, From compression molded specimens; ASTM D1693
ESCR 10% Igepal® >= 1000 hour

@Temperature 50.0 °C
>= 1000 hour

@Temperature 122 °F
F<sub>50</sub>; Condition A, From compression molded specimens; ASTM D1693
Melt Flow 4.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 10.5 MPa

@Thickness 3.17 mm
1520 psi

@Thickness 0.125 in
Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638
Flexural Modulus 0.520 GPa
75.4 ksi
1% Strain Value from rotomolded samples; ASTM D790
Impact Test 67.8 J

@Thickness 3.17 mm,
Temperature -40.0 °C
50.0 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
rotomolded; ARM Method
203 J

@Thickness 6.35 mm,
Temperature -40.0 °C
150 ft-lb

@Thickness 0.250 in,
Temperature -40.0 °F
rotomolded; ARM Method
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 42.0 °C
108 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 35.0 °C
95.0 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 170 - 215 °C
338 - 419 °F