| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N2000HL Nylon 6 (DAM).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Water Absorption | 1.6 % | 1.6 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 82.8 µm/m-°C @Temperature 20.0 °C |
46.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0590 in, BK |
| V-2 | V-2 | 0.0590 in, NC |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.5 kV/mm | 420 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 266 °C | 460 - 510 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 400 to 1400 psi | |
| Injection Rate | Fast |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 610 BT N 32 C PA610
- Palm Labs Adhesives Turbo Fuse Series 140 (200 Viscosity) Rapid Bonding Adhesive
- LATI Latishield 66-13A G/30 PA66, Steel/Glass Fiber Reinforced
- SABIC Innovative Plastics NORYL WCA871A PPE (Europe-Africa-Middle East)
- Schott FIOLAX® clear Neutral Glass Tubing
- Saint-Gobain CHR® 2045-2 Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- A. Schulman POLYBATCH™ Orange 10334 Concentrate Based In LLDPE
- BASF Neopolen® P 9435 0.07 g/cc Core density; Expanded Polypropylene (Europe)
- SABIC Innovative Plastics Noryl FXN119LG PPE+HIPS (Asia Pacific)
- 3M Novec™ 7300DL Engineered Fluid
Copyright © lookpolymers.com All Rights Reserved