- Ravago Manufacturing Americas Hylex® P1025G10 HB Polycarbonate, 10% Glass Reinforced
Ravago Manufacturing Americas Hylex® P1025G10 HB Polycarbonate, 10% Glass Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1025G10 HB Polycarbonate, 10% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Water Absorption | 0.14 % | 0.14 % | 24-Hr Immersion; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 22 - 28 g/10 min @Load 3.80 kg, Temperature 230 °C |
22 - 28 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Strength | 114 MPa | 16500 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ASTM D648 |
| Vicat Softening Point | 149 °C | 300 °F | ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.1 kV/mm @Thickness 3.17 mm |
410 kV/in @Thickness 0.125 in |
in Air; ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 254 - 271 °C | 490 - 520 °F | |
| Middle Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Front Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Nozzle Temperature | 271 - 288 °C | 520 - 550 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| 6 - 8 hour | 6 - 8 hour | with regrind | |
| Injection Pressure | 5.52 - 11.0 MPa | 800 - 1600 psi | |
| Hold Pressure | 5.52 - 8.27 MPa | 800 - 1200 psi | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | To Cylinder |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Solvay DERMALCARE® MAP L 210 Surfactant
- Solvay MIRAPOL® 550 SB Surfactant
- Polyplastics Duracon® AW-01 Acetal Co-polymer (POM), High sliding, Special lubricant, High sliding
- Valley Adhesives EM-900 High Temperature Application Glue Stick
- Wacker Silicones Geniomer® 140 Silicone TPE
- ExxonMobil Metallyte™ 28UBW-ES OPP Film
- Arlon 10292R062 Cured Silicone Rubber (Unsupported) with Polyethylene Liner
- 3M 7600 Removable Vinyl Label Material
- ExxonMobil Santoprene® 191-85PA Thermoplastic Elastomer (discontinued **)
- Haynes Hastelloy® C-22® alloy, GTAW weld, 904L base metal, C-22 weld metal
Copyright © lookpolymers.com All Rights Reserved