- Lehmann & Voss LUVOCOM® 1301-0825 PPS, linear, with carbon fiber
Lehmann & Voss LUVOCOM® 1301-0825 PPS, linear, with carbon fiber
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1301-0825 PPS, linear, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High-strength and stiff parts with low creep.Electrically conductive, suitable for continuous discharging of statically generated electricity.Suitable for metall inserts.High continuous use and heat distortion temperature. Non flammable.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ISO 1183 |
| Water Absorption | 0.050 % | 0.050 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 200 MPa | 29000 psi | |
| Elongation at Yield | 0.90 % | 0.90 % | |
| 1.2 % | 1.2 % | flexural | |
| Modulus of Elasticity | 35.0 GPa | 5080 ksi | |
| Flexural Strength | 300 MPa | 43500 psi | |
| Flexural Modulus | 30.0 GPa | 4350 ksi | |
| Coefficient of Friction, Dynamic | 0.29 | 0.29 | |
| Coefficient of Friction, Static | 0.23 | 0.23 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 9.00 µm/m-°C | 5.00 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | HOT-DISK || 60x60x3 mm |
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 240 °C | 464 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | |
| Vicat Softening Point | 260 °C | 500 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 100 ohm | <= 100 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 340 °C | 608 - 644 °F | |
| Zone 1 | 300 - 320 °C | 572 - 608 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 50.0 - 90.0 °C @Time >=14400 sec |
122 - 194 °F @Time >=4.00 hour |
|
| 100 - 140 °C @Time 7200 - 14400 sec |
212 - 284 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP HJ752 UV Polypropylene/Elastomer, Mineral Reinforced
- Chevron Phillips K-Resin® CK02 Styrene-Butadiene Copolymer, Blow Molding Grade (discontinued **)
- Kingfa JH720 G10D 10% Glass Fiber Reinforced PC
- Mitsubishi Xantar® F 22 R Polycarbonate
- Sumitomo Chemical ESPOLEX® 903 Thermoplastic Elastomer
- Plenco 4300 Phenolic, Granular, Compression Molded
- DSM Akulon® F249-HG4 Nylon 6-20% Glass Reinforced (European Grade) (Cond)
- Arkema Group Rilsan® MA 4411 Nylon 12, Flexible Tubing Grade (Conditioned)
- Arlon 920-10Bxx-P0 0.020" Self-Fusing Silicone Rubber Tape
Copyright © lookpolymers.com All Rights Reserved