Arlon 48366X007 0.007" (0.178 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 48366X007 0.007" (0.178 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 1080 FiberglassSide 2: Uncured Silicone RubberInterleave: Polyethylene This data represents typical values for the production material. The data should not be used to write, or in place of, material specificationsInformation provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.47 g/cc	0.0531 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	50.8 microns	2.00 mil	Side 1; Arlon SQA-TMS-003
	50.8 microns	2.00 mil	Side 2; Arlon SQA-TMS-003
	63.5 microns	2.50 mil	Interleave
	76.2 microns	3.00 mil	Substrate; Arlon SQA-TMS-003
	178 microns	7.00 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	66	66	Silicone Property; ASTM D2240
Tensile Strength	6.89 MPa	1000 psi	Silicone Property; ASTM D412
Elongation at Break	275 %	275 %	Silicone Property; ASTM D412
Peel Strength	0.701 kN/m	4.00 pli	Bond Strength; Arlon SQA-TMS-011

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	204 °C	400 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F
Flammability Test	0.60	0.60	[in], Flame Propagation
	0.70	0.70	[sec], After Flame Time

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Pressure 0.345 MPa, Temperature 121 °C	0.250 hour @Pressure 50.0 psi, Temperature 250 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 21.1 °C	6.00 Month @Temperature 70.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Gray
	White	Substrate
Total Product Weight (oz/yd2)	8.2	Arlon SQA-TMS-025