- Arkema Group Orgalloy® RS 6630 Polyamide 6.6 Alloy 30% Glass Fiber reinforced
Arkema Group Orgalloy® RS 6630 Polyamide 6.6 Alloy 30% Glass Fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® RS 6630 Polyamide 6.6 Alloy 30% Glass Fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Rigid grade, Nylon 6.6 basedMolding of Engineering PartsInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO R1183 |
| Water Absorption | 0.40 % | 0.40 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 23°C / 50% RH; ISO 62 |
| 2.3 % | 2.3 % | in 23°C water; ISO 62 | |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | ISO 868 |
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | ISO R527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO R527 |
| Modulus of Elasticity | 8.80 GPa | 1280 ksi | ISO R527 |
| Flexural Strength | 190 MPa | 27600 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| 210 MPa | 30500 psi | Dry; ISO 178 | |
| Flexural Modulus | 7.20 GPa | 1040 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| 7.60 GPa | 1100 ksi | Dry; ISO 178 | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
Dry; ISO 179/Af | |
| 17.0 J/cm² @Temperature -20.0 °C |
80.9 ft-lb/in² @Temperature -4.00 °F |
Dry; ISO 179/Af | |
| 18.0 J/cm² @Temperature -20.0 °C |
85.7 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 7890 MPa | 1.14e+6 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 60.0 °C |
10.0 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 20.0 - 60.0 °C |
61.1 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| Melting Point | 255 °C | 491 °F | ISO R1218 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO R75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO R75 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.10e+15 ohm-cm | 2.10e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 5.30e+15 ohm | 5.30e+15 ohm | ASTM D257 |
| Dielectric Strength | 34.0 kV/mm @Thickness 1.00 mm |
864 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Dissipation Factor | 0.016 @Frequency 100000 Hz |
0.016 @Frequency 100000 Hz |
NFC 26 230 |
| 0.029 @Frequency 100 Hz |
0.029 @Frequency 100 Hz |
NFC 26 230 | |
| 0.031 @Frequency 1000 Hz |
0.031 @Frequency 1000 Hz |
NFC 26 230 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- Rogers Corporation TMM® TMM10 Ceramic Thermoset Polymer Composite
- SABIC Innovative Plastics Lexan® 123X PC Copolymer (Europe-Africa-Middle East)
- Overview of materials for Polyethylene Terephthalate (PET), Recycled, Glass/Mineral Reinforced
- Kolon KOLEFIN® KO133MT40 M/F Reinforced Polypropylene
- Solvay RHODOLINE® 581B Surfactant
- ChevronTexaco Regal® N-68 R&O
- Diamond Polymers NYLON 6630 L Black
- Dow LDPE 609A Low Density Polyethylene, High Clarity Film Grade
- Addiplast Addilene PMD 50291 Flame Retardant Polypropylene
Copyright © lookpolymers.com All Rights Reserved