Propex Fabrics Curv™ C100A Polypropylene/Polypropylene Thermoformable Composite

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Propex Fabrics
Trade Name Curv™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Propex Fabrics Curv™ C100A Polypropylene/Polypropylene Thermoformable Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Curv™ key features include weight savings, total recyclability, no glass content, thermoformable, high impact strength, inertness, and abrasion resistance.Data provided by BP Amoco; Curv was spun off from BP Amoco in 2004 and is now a product of Propex Fabrics.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D792
0.920 g/cc
0.0332 lb/in³
ISO 1183
Water Absorption <= 0.10 %
<= 0.10 %
DIN 53495
<= 0.10 %
<= 0.10 %
20°C; ASTM D570-81
<= 0.10 %
<= 0.10 %
100°C; ASTM D570-81
Mechanical Properties Metric English Comments
Ball Indentation Hardness 35.0 MPa
5080 psi
EN ISO 2039-1
Tensile Strength, Ultimate 120 MPa
17400 psi
MD; DIN EN ISO 527
120 MPa
17400 psi
CD; DIN EN ISO 527
180 MPa
26100 psi
ASTM D638M-92
Elongation at Break 16.6 %
16.6 %
ASTM D638M-92
20 %
20 %
MD; DIN EN ISO 527
20 %
20 %
CD; DIN EN ISO 527
Tensile Modulus 4.20 GPa
609 ksi
MD; DIN EN ISO 527
4.20 GPa
609 ksi
CD; DIN EN ISO 527
5.00 GPa
725 ksi
ASTM D638M-93
Flexural Strength 80.0 MPa
11600 psi
MD; DIN EN ISO 178
80.0 MPa
11600 psi
CD; DIN EN ISO 178
107.7 MPa
15620 psi
ASTM D790M-93
Flexural Modulus 3.50 GPa
508 ksi
MD; DIN EN ISO 178
3.50 GPa
508 ksi
CD; DIN EN ISO 178
3.60 GPa
522 ksi
ASTM D790M-93
Compressive Strength >= 300 MPa
>= 43500 psi
Normal to Plane; EN ISO 604
Izod Impact, Notched 47.5 J/cm
89.0 ft-lb/in
ASTM D256-93a
75.0 J/cm

@Temperature -40.0 °C
141 ft-lb/in

@Temperature -40.0 °F
ASTM D256-93a
Izod Impact, Notched (ISO) 400 kJ/m²
190 ft-lb/in²
22 J; EN ISO 180/2 ep b
600 kJ/m²

@Temperature -40.0 °C
286 ft-lb/in²

@Temperature -40.0 °F
22 J; EN ISO 180/2 ep b
Izod Impact, Unnotched (ISO) NB
NB
22 J; EN ISO 180/2 ep
Charpy Impact Unnotched NB
NB
EN ISO 179/2 ep
NB
NB
Low Temp; EN ISO 179/2 ep
Charpy Impact, Notched 12.0 J/cm²
57.1 ft-lb/in²
EN ISO 179/2 ep b
Tensile Impact Strength 1000 kJ/m²
476 ft-lb/in²
MD; EN ISO 8256
1000 kJ/m²
476 ft-lb/in²
CD; EN ISO 8256
Puncture Energy 17.6 J
13.0 ft-lb
70°C High Speed Puncture Energy; ASTM D3763-97a
21.6 J
15.9 ft-lb
100°C High Speed Puncture Energy; ASTM D3763-97a
40.0 J
29.5 ft-lb
Puncture Impact; 52 J; 2.1 mm; ISO 6603
14.1 J

@Temperature -40.0 °C
10.4 ft-lb

@Temperature -40.0 °F
High Speed Puncture Energy; ASTM D3763-97a
Torsional Stiffness 1200 MPa
174000 psi
DIN EN ISO 6721
Thermal Properties Metric English Comments
CTE, linear 41.0 µm/m-°C

@Temperature 20.0 °C
22.8 µin/in-°F

@Temperature 68.0 °F
Temp range not reported; ASTM D696
68.0 µm/m-°C

@Temperature 20.0 - 80.0 °C
37.8 µin/in-°F

@Temperature 68.0 - 176 °F
DIN 53752
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
flatwise; EN ISO 75-2B
160 °C
320 °F
ASTM D648-82/88
Deflection Temperature at 1.8 MPa (264 psi) 102 °C
216 °F
ASTM D648-82/88
102 °C
216 °F
flatwise; EN ISO 75-2A
Vicat Softening Point 175 °C
347 °F
50K/h; DIN EN ISO 306
Descriptive Properties Value Comments
Fire Behavior of Building Materials Passed B 2
DIN 4102