- Samsung Cheil Industries Starex® SF-0505HWR MABS, Unreinforced Scratch Resistant
Samsung Cheil Industries Starex® SF-0505HWR MABS, Unreinforced Scratch Resistant
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SF-0505HWR MABS, Unreinforced Scratch Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 19 g/10 min @Load 10.0 kg, Temperature 220 °C |
19 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength at Break | 32.4 MPa | 4700 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 43.1 MPa | 6260 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 21 % | 21 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.06 GPa | 299 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 6.35 mm |
2.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.37 J/cm @Thickness 3.17 mm |
2.57 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 6.40 mm |
181 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | B/50; ISO R306 |
| 92.0 °C | 198 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Pencil Hardness | HB | 500g, JIS K 5401 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Z85T Hydrogenated NBR Compound
- SABIC Innovative Plastics Lexan® 955U PC
- ExxonMobil Santoprene® 221-55 Thermoplastic Elastomer (discontinued **)
- SABIC Innovative Plastics NORYL ZWM2411 PPE+PS (Asia Pacific)
- Borealis Visico™/Visico™ LE4423/LE4438 Polyethylene Compound, Crosslinkable
- DuPont Elvax® 360 Ethylene-Vinyl Acetate Copolymer Resin
- ExxonMobil 46 Mobil EAL Arctic Series
- Chosun Refractories CTL-Z2 Monolithic Refractories for Ladle and Tundish
- Fainplast Compounds CKL 0221/T Flexible PVC, Sheathing Lead Free
Copyright © lookpolymers.com All Rights Reserved