Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
Manufacturer | Polyram |
Trade Name | |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Polyram RamTough PZ305G4 Polycarbonate, 20% Glass Fiber.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
Water Absorption at Saturation | 0.10 % | 0.10 % | ISO 62 |
Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ISO 2577 |
Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 70.0 MPa | 10200 psi | ISO 527 |
Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
Tensile Modulus | 4.00 GPa | 580 ksi | ISO 527 |
Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
Flexural Modulus | 4.80 GPa | 696 ksi | ISO 178 |
Izod Impact, Notched (ISO) | 12.5 kJ/m² | 5.95 ft-lb/in² | ISO 180 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75 |
Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ISO 75 |
Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60250 |