Seals Eastern 5243 Neoprene / Chloroprene
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Seals Eastern, Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Seals Eastern 5243 Neoprene / Chloroprene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose neopreneInformation provided by Seals Eastern, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D297, 15 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 65 | >= 65 | ASTM D2240, Type A |
| 75 | 75 | AVG; ASTM D2240, Type A | |
| Tensile Strength at Break | >= 13.42 MPa | >= 1947 psi | ASTM D412 Method A |
| 17.95 MPa | 2603 psi | AVG; ASTM D412 Method A | |
| Tensile Strength, Yield | >= 1.02 MPa | >= 148 psi | Stress at Elongation M50; ASTM D412 Method A |
| 1.23 MPa | 179 psi | AVG Stress at Elongation M25; ASTM D412 Method A | |
| >= 1.40 MPa | >= 203 psi | Stress at Elongation M100; ASTM D412 Method A | |
| 2.02 MPa | 293 psi | AVG Stress at Elongation M50; ASTM D412 Method A | |
| 4.01 MPa | 582 psi | AVG Stress at Elongation M100; ASTM D412 Method A | |
| Elongation at Break | >= 194 % | >= 194 % | ASTM D412 Method A |
| 312 % | 312 % | AVG; ASTM D412 Method A | |
| Modulus of Elasticity | 0.007453 GPa | 1.081 ksi | ASTM D412 Method A |
| Shear Modulus | 0.00248 GPa | 0.360 ksi | ASTM D412 Method A |
| Secant Modulus | 0.007012 GPa | 1.017 ksi | ASTM D412 Method A |
| Tear Strength Test | 293 | 293 | (psi); ASTM D624, Die B |
| Compression Set | 31 % @Temperature 125 °C, Time 252000 sec |
31 % @Temperature 257 °F, Time 70.0 hour |
ASTM D395, Test B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D1329 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Strain Energy / Unit Volume at 20% Elongation (psi) | 20 |
Users viewing this material also viewed the following:
- PolyOne Nanoblend™ MB 1201 Polypropylene Impact Copolymer (PP Impact Copolymer)
- Total Evatane® 24 - 03 HDPE vinyl acetate copolymer, blown film, injection molding (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66 (Asia Pacific)
- CP-Polymer-Technik Wellamid® 6000 CF 18 HWCP 18% Carbon Fiber Nylon 6, Heat Stabilized, Conditioned
- ExxonMobil Label-Lyte® 155 LL-534 Coated, Clear OPP Facestock
- BASF Lupranate® MS Isocyanate
- Bulk Molding Compounds BMC 610 Mineral Filled, Glass Reinforced Polyester Compound
- BASF Neopolen® P 8015 0.03 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved