- DuPont Performance Polymers VTR 8710 (ETP-600S) Peroxide Cured Fluoroelastomer (FKM) Formulation (discontinue
DuPont Performance Polymers VTR 8710 (ETP-600S) Peroxide Cured Fluoroelastomer (FKM) Formulation (discontinue
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers VTR 8710 (ETP-600S) Peroxide Cured Fluoroelastomer (FKM) Formulation
(discontinue.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationViton® Extreme™ ETP-600S
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 63 @Temperature 121 °C |
63 @Temperature 250 °F |
ML 1 + 10 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 79 | 79 | Cured 7 min at 177°C and Post Cured 16 hr at 200°C |
| Tensile Strength, Ultimate | 19.0 MPa | 2760 psi | Cured 7 min at 177°C and Post Cured 16 hr at 200°C |
| Elongation at Break | 202 % | 202 % | Cured 7 min at 177°C and Post Cured 16 hr at 200°C |
| 50% Modulus | 0.00360 GPa | 0.522 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 200°C |
| 100% Modulus | 0.00880 GPa | 1.28 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 200°C |
| Compression Set | 43 % @Temperature 200 °C |
43 % @Temperature 392 °F |
Method B, O-rings 70 hr at 200°C (Post Cured 16 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -7.00 °C | 19.4 °F | TR-10 |
| Glass Transition Temp, Tg | -11.0 °C | 12.2 °F | MDSC |
Users viewing this material also viewed the following:
- Reliance Industries Repol H007EG Polypropylene
- Lehmann & Voss LUVOCOM® 1301-8349 PPS, linear, with PTFE
- LG Chemical LUPOS GP-2106F General Purpose ABS, 10% Glass Fiber Reinforced, Weather Resistant, Flame Retardant
- SABIC Innovative Plastics ULTEM MD131A PEI
- Solvay IGEPAL® CO 890 Surfactant
- Silberline Stamford "A3"
- A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer
- Covestro Bayflex® 180 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- AK Steel ASTM A 570, Grade 55 Hot Rolled Carbon Steel, Structural Quality (SQ)
- BASF Ultramid® B3GM35 BK 30564 15/25% Glass/Mineral Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved