Polyram RamTal PM1113 Polyacetal Copolymer for Injection Molding

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer Polyram
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polyram RamTal PM1113 Polyacetal Copolymer for Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General purpose polyacetal copolymer for injection molding applications, MFI 13.Information provided by Polyram.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Water Absorption at Saturation 0.22 %
0.22 %
ISO 62
Linear Mold Shrinkage 0.018 - 0.022 cm/cm
0.018 - 0.022 in/in
ISO 2577
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 13 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 82
82
Tensile Strength, Yield 65.0 MPa
9430 psi
ISO 527
Elongation at Break 25 %
25 %
ISO 527
Flexural Strength 85.0 MPa
12300 psi
ISO 178
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
ISO 75
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Flame Spread 18 mm/min
0.71 in/min
FMVSS302
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
 3.8

@Frequency 1.00e+6 Hz
 IEC 60250
Dielectric Strength 24.0 kV/mm
610 kV/in
IEC 60250