- Samsung Cheil Industries Starex® SP-0170 ABS, Unreinforced Extrusion Grade
Samsung Cheil Industries Starex® SP-0170 ABS, Unreinforced Extrusion Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SP-0170 ABS, Unreinforced Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 7.1 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.1 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength, Yield | 38.2 MPa | 5550 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 50 % | 50 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 53.0 MPa | 7690 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.72 GPa | 249 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 3.82 J/cm @Thickness 6.35 mm |
7.16 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 4.71 J/cm @Thickness 3.17 mm |
8.82 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HFD1810 PC Copolymer (Europe-Africa-Middle East)
- LNP Thermocomp® EF-1002 EP BK8-114 Polyetherimide, Glass Fiber Reinforcement (discontinued **)
- IBC Advanced Alloys 10% BeCu Beryllium Copper Master Alloy
- Gwent Electronic Materials C2070424P2 Carbon Graphite Ink
- Multibase Multi-Flex® D 4502 TPO Thermoplastic Polyolefin Elastomer
- SABIC Innovative Plastics LNP LUBRICOMP RAL23 PA 66 (Europe-Africa-Middle East)
- SABIC Innovative Plastics Valox® VX8015U PBT+PET (Europe-Africa-Middle East)
- ExxonMobil Teresstic 32
- Hexcel® HexPly® F522 Epoxy Resin, T2C145 Carbon Tape
Copyright © lookpolymers.com All Rights Reserved