Polyram RamSter PF300G9 PBT, 45% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamSter PF300G9 PBT, 45% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
45% Glass fiber reinforced PBT for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | ISO 2577 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 250 °C |
10 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 13.7 GPa | 1990 ksi | ISO 527 |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Glow Wire Test | 650 °C | 1200 °F | GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Cookson Group Plaskon® 3300SH Mineral Filled Epoxy Molding Compound (discontinued **)
- Sharadaa Ceramics Sharada RFC-95 Gel Bonded Castables
- Solvay Chemicals Strontium carbonate standard powder
- A. Schulman PAPERMATCH® H-5338 Specialty Masterbatch
- DuPont Conpol™ 4R11S1 Ethylene-Methacrylic Acid Additive Resin
- Plenco 4504 Phenolic, Granular, Injection Molded
- CLAL-MSX NICLAFOR® 1000 TH3 Quenched/Cold Rolled/Precipitation Heat Treated, Rolled Copper Alloy
- A.D. Compound Adene NCJA Homopolymer 30% CaCO3 Filled Polypropylene
- Ravago Manufacturing Americas Hylex® P1310G40 HB Polycarbonate, 40% Fiberglass Reinforced, UV Stabilized
Copyright © lookpolymers.com All Rights Reserved