Polyram RamShine PS580 High Impact Polystyrene, Flame Retardant
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamShine PS580 High Impact Polystyrene, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant V-0, high impact polystyrene for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ISO 2577 |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 200 °C |
20 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
| Elongation at Break | 60 % | 60 % | ISO 527 |
| Tensile Modulus | 1.50 GPa | 218 ksi | ISO 527 |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 |
| Vicat Softening Point | 80.0 °C | 176 °F | ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJJC340U Polyvinyl Chloride, Flexible (PVC, Flexible)
- Nye Lubricants 717E(RL) Rheolube Grease
- Lehmann & Voss LUVOCOM® 80-8222 Polyacetal-copolymer, with mineral filler, lubricant modified
- Kennametal Stellite Nucalloy® 453 High-Silicon Nickel-Base Hardfacing Alloy
- Cossa Polimeri ESTADIENE 1016 HT V0 Flame Retardant ABS
- Eurostar Staramide PFB42 PA6 Injection Molding Resin
- Covestro Makrolon® DP1-1888* Polycarbonate, 20% Glass Filled
- Bhansali Engineering Santron IMS 2000 Glitter SAN Resin
- Permabond 910FS Cyanoacrylate, Methyl grade
Copyright © lookpolymers.com All Rights Reserved