- Quadrant EPP KETRON® MD PEEK, A Metal-Detectable Polyetheretherketone
Quadrant EPP KETRON® MD PEEK, A Metal-Detectable Polyetheretherketone
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced |
| Manufacturer | Quadrant Engineering Plastics Products |
| Trade Name | Ketron® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quadrant EPP KETRON® MD PEEK, A Metal-Detectable Polyetheretherketone.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc @Temperature 22.8 °C |
1.36 g/cc @Temperature 73.0 °F |
ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | IMMERSION; 24HRS.; ASTM D570 2 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ASTM D570 2 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 86.2 MPa @Temperature 22.8 °C |
12500 psi @Temperature 73.0 °F |
ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 4.14 GPa @Temperature 22.8 °C |
600 ksi @Temperature 73.0 °F |
ASTM D792 |
| Flexural Strength | 152 MPa @Temperature 22.8 °C |
22000 psi @Temperature 73.0 °F |
ASTM D790 |
| Flexural Modulus | 4.34 GPa @Temperature 22.8 °C |
630 ksi @Temperature 73.0 °F |
ASTM D790 |
| Compressive Modulus | 0.138 GPa @Temperature 22.8 °C |
20.0 ksi @Temperature 73.0 °F |
|
| 2.90 GPa @Temperature 22.8 °C |
420 ksi @Temperature 73.0 °F |
||
| Shear Strength | 82.7 MPa @Temperature 22.8 °C |
12000 psi @Temperature 73.0 °F |
ASTM D732 |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | QTM 55007 |
| Limiting Pressure Velocity | 0.420 MPa-m/sec | 12000 psi-ft/min | (with 4:1 safety factor applied); QTM 55007 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 340 °C | 644 °F | ASTM D3418 |
Users viewing this material also viewed the following:
- Radici Raditer® B RVA 100 Polybutylene Terephthalate with 10% Glass fiber
- Freudenberg Simrit Simriz® 485 Universal FFKT Perfluoroelastomer Compound
- SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS (Asia Pacific)
- Techmer ES Plastiblend® PA6/ABS 1120 GF20 20% Glass Filled
- Wellman Wellamid® XT1668-BK1 High Impact Nylon 66
- ExxonMobil 111 Mobilux EP
- Eagle Brass 101 OFE COPPER (Certified), 3/4 Hard
- 3M 32666 Tan Heavy Duty Performance Coating - Part B
- Amco PRIMATOP PP CO 220-23 Impact Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved