ExxonMobil LDPE LD 362ON Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Exxon Chemical
Trade Name	LDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LDPE LD 362ON Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 362 series are LEVA LDPE grades, offering good mechanical and sealing properties. Several additive combinations are available according to the required surface properties.Availability: Africa & Middle East and Europe Additive: Antiblock: 1700 ppmSlip: NoThermal Stabilizer: YesApplications: Agricultural FilmCo-Extrusion FilmsFoamsForm Fill and Seal PackagingFreezer FilmHigh Clarity FilmLamination FilmPoultry BagRice BagsRubber Bale WrapInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.928 g/cc	0.0335 lb/in³	ExxonMobil method
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	1750 ppm	1750 ppm

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	310 %	310 %	ASTM D882
Film Elongation at Break, TD	520 %	520 %	ASTM D882
Elmendorf Tear Strength MD	90 g	90 g	ASTM D1922
Elmendorf Tear Strength TD	90 g	90 g	ASTM D1922
Dart Drop Test	170 g	0.375 lb	ASTM D1709A
Film Tensile Strength at Break, MD	28.3 MPa	4100 psi	ASTM D882
Film Tensile Strength at Break, TD	22.1 MPa	3200 psi	ASTM D882
1% Secant Modulus, MD	159 MPa	23000 psi	ASTM D882
1% Secant Modulus, TD	179 MPa	26000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 219 °C	<= 426 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	5.0 %	5.0 %	ASTM D1003