Polyram PlusTek PB145 Nylon 6, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PB145 Nylon 6, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 6 for fast cycle injection moldingInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DIN 53479 |
| Water Absorption | 9.5 % | 9.5 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.012 - 0.016 cm/cm | 0.012 - 0.016 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM-D785 |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ASTM-D638 |
| Elongation at Break | 20 % | 20 % | ASTM-D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.500 J/cm @Temperature 23.0 °C |
0.937 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous Use |
| 180 °C | 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | DIN 53461 |
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 100 kV/mm | 2540 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® AT-20GB/000 Acetal-Copolymer, Glass Bead Filled (discontinued **)
- Zircar Zirconia ZYZ-3 Zirconia Boards and Discs Insulation
- Overview of materials for Cyclo Olefin Polymer
- Solvay Chemicals NOCOLOK® CB Flux Potassium Silicofluoride
- SABIC Innovative Plastics Ultem ATX100R PEI (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP OE004A PPS - BRANCHED (Europe-Africa-Middle East)
- Tipco Tipcolene® FPC 10 PPC - 10% Calcium Carbonate Reinforced Polypropylene Copolymer
- Eagle Brass 725 Copper Nickel Tin, 1/2 Hard
- CP-Polymer-Technik Wellamid® 6000 MF 30 HWCP 30% Milled Glass Fiber Nylon 6, Heat Stabilized, Dry
- California Fine Wire Alloy 422 Precious Metal Alloy
Copyright © lookpolymers.com All Rights Reserved