Polyram PlusTek PA840G7 Nylon 6.6 for Injection Molding, 35% Glass Fibers Reinforced, Impact Modified

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade
Manufacturer Polyram
Trade Name PlusTek
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polyram PlusTek PA840G7 Nylon 6.6 for Injection Molding, 35% Glass Fibers Reinforced, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
35% Glass fiber reinforced, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.7 %
1.7 %
50% RH; ISO 62
Water Absorption at Saturation 5.6 %
5.6 %
ISO 62
Linear Mold Shrinkage 0.0030 - 0.0070 cm/cm
0.0030 - 0.0070 in/in
ISO 2577
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
Tensile Strength, Yield 155 MPa
22500 psi
ISO 527
Elongation at Break 3.0 %
3.0 %
ISO 527
Flexural Strength 220 MPa
31900 psi
ISO 178
Flexural Modulus 7.50 GPa
1090 ksi
ISO 178
Izod Impact, Notched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 256 °C
493 °F
ISO 11357
Maximum Service Temperature, Air 110 °C
230 °F
Continuous use
250 °C
482 °F
Short peaks operation
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
ISO 75
Flammability, UL94 HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 90.0 kV/mm
2290 kV/in
IEC 60250