Polyram PlusTek PA7800G33 Nylon 6.6 for Injection Molding, 33% Glass Fiber Reinforced, Heat Stabilized, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA7800G33 Nylon 6.6 for Injection Molding, 33% Glass Fiber Reinforced, Heat Stabilized, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
33% Glass fiber reinforced, heat stabilized, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.5 % | 4.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 157 MPa | 22800 psi | ISO 527 |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527 |
| Tensile Modulus | 8.81 GPa | 1280 ksi | ISO 527 |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| Flexural Modulus | 8.55 GPa | 1240 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² @Temperature -30.0 °C |
9.04 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 22.5 kJ/m² @Temperature 23.0 °C |
10.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C2100 PC+ABS (Europe-Africa-Middle East)
- Albis Plastics Tedur® L 9521-1 PPS, 60% Glass Fiber/Mineral (discontinued **)
- Honeywell Aegisâ„¢ H135ZP Nylon 6 Extrusion Grade Homopolymer Film
- SK Chemicals SKYPET® BR8040 Low Content CHDM Modified Copolyester Resin
- Borealis RA130E-2491 Polypropylene Random Copolymer
- Lubrizol ESTANE® GP95AB Ester Based Thermoplastic Polyurethane
- ExxonMobil Exxtral™ CMU 201 Performance Polyolefin
- ExxonMobil HD 6719.62 Injection Molding Resin
- DuPont™ Kapton® 50HN Polyimide Film, 13 Micron Thickness
- ConocoPhillips Conoco® El Mar® Grade 30 Mid Ash Supreme Oil
Copyright © lookpolymers.com All Rights Reserved