Teijin Panlite® GS-3430 Friction and Abrasion Resistant, Glass Fiber Reinforced Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled
Manufacturer Teijin
Trade Name Panlite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teijin Panlite® GS-3430 Friction and Abrasion Resistant, Glass Fiber Reinforced Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
GF 30% reinforced grade, meeting UL 94 V-2. It is compounded with fluorine powder to improve friction and abrasion resistance, maintaining excellent characteristics of polycarbonate resin.Applications:Mechanical, electric and electronic components that need abrasion and friction resistance.Information provided by Teijin Chemicals Ltd.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Water Absorption 0.10 %
0.10 %
in water, 23°C, 24h; ISO 62
Linear Mold Shrinkage 0.00020 - 0.0020 cm/cm

@Thickness 4.00 mm
 0.00020 - 0.0020 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Thickness 4.00 mm
 0.0030 - 0.0050 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
50mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
50mm/min; ISO 527
Tensile Modulus 8.00 GPa
1160 ksi
1mm/min; ISO 527
Flexural Strength 155 MPa
22500 psi
2mm/min; ISO 178
Flexural Modulus 7.30 GPa
1060 ksi
2mm/min; ISO 178
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Temperature 20.0 °C
 11.1 µin/in-°F

@Temperature 68.0 °F
 ISO 11359
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 20.0 °C
 33.3 µin/in-°F

@Temperature 68.0 °F
 ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 148 °C
298 °F
ISO 75
Vicat Softening Point 152 °C
306 °F
50°C/hr, 50N; ISO 306
UL RTI, Electrical 130 °C

@Thickness 1.47 mm
 266 °F

@Thickness 0.0579 in
 UL 746B
UL RTI, Mechanical with Impact 120 °C

@Thickness 1.47 mm
 248 °F

@Thickness 0.0579 in
 UL 746B
UL RTI, Mechanical without Impact 130 °C

@Thickness 1.47 mm
 266 °F

@Thickness 0.0579 in
 UL 746B
Flammability, UL94 V-2

@Thickness 0.380 mm
 V-2

@Thickness 0.0150 in
V-1

@Thickness 3.00 mm
 V-1

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 100 Hz
 3.5

@Frequency 100 Hz
 IEC 60250
3.5

@Frequency 1e+6 Hz
 3.5

@Frequency 1e+6 Hz
 IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243
Dissipation Factor 0.0010

@Frequency 100 Hz
 0.0010

@Frequency 100 Hz
 IEC 60250
0.0090

@Frequency 1e+6 Hz
 0.0090

@Frequency 1e+6 Hz
 IEC 60250
Comparative Tracking Index 175 V
175 V
IEC 60112