PolyOne Therma-Tech™ NJC-6000 TC Nylon 12 (discontinued **)

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Therma-Tech™ NJC-6000 TC Nylon 12 (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of thermoplastics. These materials provide the benefits of proprietary conductive additive technologies and the performance of select engineering thermoplastic resins. Therma-Tech compounds have been shown to improve thermal conductivity up to 100-times that of conventional plastics and can be used in a wide range of thermal management applications.

Physical Properties	Metric	English	Comments
Specific Gravity	1.58 g/cc	1.58 g/cc	ASTM D792
Water Absorption	0.10 % @Thickness 3.18 mm, Time 86400 sec	0.10 % @Thickness 0.125 in, Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0030 - 0.0040 cm/cm	0.0030 - 0.0040 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	49.0 MPa	7110 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	0.90 %	0.90 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	19.3 GPa	2800 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	103 MPa	14900 psi	ASTM D790
Flexural Modulus	19.4 GPa	2810 ksi	ASTM D790
Izod Impact, Notched	0.267 J/cm @Thickness 6.35 mm, Temperature 23.0 °C	0.500 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Thermal Conductivity	11.0 W/m-K	76.3 BTU-in/hr-ft²-°F	ASTM C177
Deflection Temperature at 0.46 MPa (66 psi)	193 °C @Thickness 6.35 mm	379 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	185 °C @Thickness 6.35 mm	365 °F @Thickness 0.250 in	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	100 - 1000 ohm-cm	100 - 1000 ohm-cm	ASTM D257
Surface Resistance	10 - 100 ohm	10 - 100 ohm	ASTM D257

Processing Properties	Metric	English	Comments
Melt Temperature	260 - 277 °C	500 - 531 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F

Descriptive Properties	Value	Comments
Features	Electrically Conductive
	Thermally Conductive
Forms	Pellets
Generic Name	Polyamide 12 (Nylon 12)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Automotive Applications
	Automotive Under the Hood
	Consumer Applications
	Electrical/Electronic Applications
	Housings
	Industrial Applications