Polyram PlusTek PA201 Nylon 66 for Extrusion
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Extruded |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA201 Nylon 66 for Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High viscosity Nylon 66 for extrusion applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 2.5 % | 2.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.013 - 0.017 cm/cm | 0.013 - 0.017 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 265 °C | 509 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 |
| Dielectric Strength | 30.5 kV/mm | 775 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Honeywell ACLAR® 22C (5.00 mil) Copolymer Film (discontinued **)
- SABIC Innovative Plastics NORYL GFN3 PPE+HIPS (Asia Pacific)
- The NanoSteel® Company SHS 8000 TWAS Iron Based Alloy, Cored Wire
- A. Schulman COMTUF® 464 Glass Reinforced Impact Modified PBT Alloy
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 90A, Non-Black Sulfur Cure
- Dow LDPE 609A Low Density Polyethylene, High Clarity Film Grade
- Fainplast Compounds GS 7004 Flexible PVC, Injection Molding for Footwear
- ExxonMobil Bicor® 120 LTSC OPP Film
- E-Polymers SEPAZ® C230GP 30% Glass Fiber Reinforced LCP Resin
- BASF N,N-Dimethylacetamide
Copyright © lookpolymers.com All Rights Reserved