- A. Schulman SCHULAMID® 66 GB40 40% Glass Bead Reinforced Nylon 66
A. Schulman SCHULAMID® 66 GB40 40% Glass Bead Reinforced Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 66 GB40 40% Glass Bead Reinforced Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.175 mm |
0.011 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 4.96 GPa | 720 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 209 °C | 408 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
| Moisture Content | 0.080 - 0.12 % | 0.080 - 0.12 % |
Users viewing this material also viewed the following:
- RheTech Products G13P100-00UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, Natural
- LNP VALOX® SMV5846 PBT + PET Alloy, 20% Carbon Fiber Reinforcement (discontinued **)
- Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 61 Shore A (discontinued **)
- NIZHNEKAMSKNEFTEKHIM PE 6949C (486H3) High Density Polyethylene
- Teijin Multilon TN-7100F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
- ELASTO UK Dryflex® 650900 TPE, Improved Compression Set and High Temperature Resistance, 90A Hardness
- EMS-Grivory Grivory® GV-5H EF black 9915 PA*-GF50
- CP-Polymer-Technik Wellamid® 6600 GV 45 HWCP 45% Glass Fiber Nylon 66, Heat Stabilized, Conditioned
- ExxonMobil Geolast® 701-87W183 Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved