Polyplastic Armlen® PP 12IM-895 Impact Modified Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded |
| Manufacturer | Polyplastic Group |
| Trade Name | Armlen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyplastic Armlen® PP 12IM-895 Impact Modified Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact modified polypropylene composite materialUV resistantInformation provided by PolyPlastic Group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0076 cm/cm | 0.0076 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0011 cm/cm | 0.0011 in/in | ISO 294-4 |
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 230 °C |
21 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-2 |
| Elongation at Break | 90 % | 90 % | ISO 527-1/-2 |
| Flexural Strength | 23.0 MPa | 3340 psi | ISO 178 |
| Flexural Modulus | 1.57 GPa | 228 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -20.0 °C |
4.28 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 230 °C | 428 - 446 °F | |
| Mold Temperature | 60.0 °C | 140 °F |
Users viewing this material also viewed the following:
- Sibur APP-G Atactic Polypropylene
- Shinkong Synthetic Fibers Shinite® E202G30 PBT, 30% Glass Filled
- A. Schulman POLYBATCH™ White LL8970 TS Concentrate Based In LLDPE
- Ensinger Tecaform™ Acetal Copolymer - Extruded Products (POM)
- Axiall 14820 Wire & Cable Flexible PVC
- 3M 2A804 High Performance Temporary Surface Protection Tape
- Arlon 51576R016A 0.016" (0.406 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- BASF Ultramid® B3GM35 BK 60564 40% Glass/Mineral Filled PA6 (Conditioned)
- Bhansali Engineering Abstron KU600N ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved