Polyplastic Armamid® PA GF50-1 Nylon 6, 50% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Polyplastic Group |
| Trade Name | Armamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyplastic Armamid® PA GF50-1 Nylon 6, 50% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High stiffnessInformation provided by PolyPlastic Group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Water Absorption | 0.95 % @Time 86400 sec |
0.95 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | <= 0.0020 cm/cm | <= 0.0020 in/in | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 37 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 37 |
| Flexural Strength | 290 MPa | 42100 psi | ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature -40.0 °C |
30.9 ft-lb/in² @Temperature -40.0 °F |
ISO 179/1eU |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -40.0 °C |
4.28 ft-lb/in² @Temperature -40.0 °F |
ISO 179/1eA |
| 1.20 J/cm² @Temperature 20.0 °C |
5.71 ft-lb/in² @Temperature 68.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
IEC 60695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 270 °C | 500 - 518 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 85.0 °C @Time 7200 - 14400 sec |
185 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- Plenco 5303 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP RBL36XXJ PA 66
- Shanghai Ofluorine J-2 PVDF Extrusion Grade
- SABIC Innovative Plastics LNP THERMOCOMP AF004AH ABS
- TIMET TIMETAL® 550 (Ti-4Al-4Mo-2Sn) Titanium Alloy Solution Treated
- Corbion Purac Blend C High Heat, Impact Modified Homopolymer PLA
- CP-Polymer-Technik Wellamid® 6000 MX 400 CP Combination Nylon 6, Heat Stabilized, Conditioned
- DuPont Teijin Films Melinex® 377 Polyester Film, 500 Gauge
- Orion Engineered Carbons CORAX® N 121 ASTM Carbon Black
- Universal Wire Works No. 12 Cobalt Alloy Welding Wire
Copyright © lookpolymers.com All Rights Reserved