Polymer Resources PPX-GP4-IM Modified-PPO, Impact Modified

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Impact Grade
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-GP4-IM Modified-PPO, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified-Polyphenylene Oxide, Impact Modified, 210F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 20 - 30 g/10 min

@Load 11.6 kg,
Temperature 250 °C
20 - 30 g/10 min

@Load 25.6 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D638
Tensile Strength, Yield 34.5 MPa
5000 psi
ASTM D638
Elongation at Break 70 %
70 %
ASTM D638
Flexural Strength 48.3 MPa
7000 psi
ASTM D790
Flexural Modulus 1.76 GPa
255 ksi
ASTM D790
Izod Impact, Notched 1.87 J/cm

@Temperature -40.0 °C
3.50 ft-lb/in

@Temperature -40.0 °F
ASTM D256
2.67 J/cm

@Temperature -17.8 °C
5.00 ft-lb/in

@Temperature 0.000 °F
ASTM D256
3.74 J/cm

@Temperature 22.8 °C
7.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Gardner Impact 22.6 J
16.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 98.9 °C
210 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 93.3 °C
200 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 249 - 299 °C
480 - 570 °F
Middle Barrel Temperature 260 - 304 °C
500 - 580 °F
Front Barrel Temperature 271 - 310 °C
520 - 590 °F
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 71.1 - 98.9 °C
160 - 210 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0015