Polymer Resources PC-HH-UV Polycarbonate, High Heat, UV-stabilized
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, High Heat |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC-HH-UV Polycarbonate, High Heat, UV-stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, High Heat, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 2.0 - 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 - 5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.12 MPa | 10750 psi | ASTM D638 |
| Tensile Strength, Yield | 66.2 MPa | 9600 psi | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 3.74 J/cm @Temperature 22.8 °C |
7.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 11.3 J | 8.33 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.59 mm |
V-2 @Thickness 0.0626 in |
|
| V-2 @Thickness 3.17 mm |
V-2 @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 299 - 338 °C | 570 - 640 °F | |
| Middle Barrel Temperature | 299 - 338 °C | 570 - 640 °F | |
| Front Barrel Temperature | 327 - 371 °C | 620 - 700 °F | |
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | |
| Mold Temperature | 76.7 - 98.9 °C | 170 - 210 °F | |
| Drying Temperature | 121 - 129 °C | 250 - 265 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- RheTech Products HP513-00A High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
- SABIC Innovative Plastics Lexan® LUX9616G PC (Europe-Africa-Middle East)
- Meilian Chemical PE62071 RED MASTERBATCH
- Iran Petrochemical (PCC) I3 HC 7260(THE) High Density Polyethylene
- Teknor Apex Telcar® TL-1472A Thermoplastic Elastomer
- UBE F522 Polyethylene
- EMS-Grivory Grivory® LV-23 ESD PA12-GF23
- DuPont Performance Polymers VTR 8655 (GBL-S) Peroxide Cured Fluoroelastomer (FKM) (discontinued **)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR Mistron Vapor Filler
Copyright © lookpolymers.com All Rights Reserved