Polymer Resources NY66-FRG25 Flame Retardant Nylon 66, 25% Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources NY66-FRG25 Flame Retardant Nylon 66, 25% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 66, 25% Glass Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 159 MPa | 23000 psi | ASTM D638 |
| Tensile Strength, Yield | 159 MPa | 23000 psi | ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 22.8 °C |
1.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 263 °C | 505 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0626 in |
|
| V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Middle Barrel Temperature | 282 - 299 °C | 540 - 570 °F | |
| Front Barrel Temperature | 282 - 304 °C | 540 - 580 °F | |
| Melt Temperature | 288 - 304 °C | 550 - 580 °F | |
| Mold Temperature | 82.2 - 104 °C | 180 - 220 °F | |
| Drying Temperature | 73.9 - 85.0 °C | 165 - 185 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA-924 Impact Modified Acrylic Resin
- Lehmann & Voss LUVOCOM® 1502-7867/BL4 PPSU, unreinforced
- Latrobe Tatmoâ„¢ ASTM M1 High Speed Steel
- Iran Petrochemical (PCC) LL0220AA Linear Low Density Polyethylene
- Shin-Etsu Silicones KSP-101 Fluid
- DuPont Performance Polymers Crastin® 6129 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- DuPont Elvax® 3176CW-3 Ethylene Vinyl Acetate (discontinued **)
- Karina 802D35/1-E-AC-LF Ivory PVC Compound
Copyright © lookpolymers.com All Rights Reserved