Polykemi AB SCANMID 6 B12^ F50 Nylon 6, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Polykemi AB |
| Trade Name | SCANMID 6 |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANMID 6 B12^ F50 Nylon 6, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Filler Content | 50 % | 50 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | With Flow; ISO 2577 |
| 0.0080 cm/cm | 0.0080 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 81 @Time 15.0 sec |
81 @Time 0.00417 hour |
ASTM D2240 |
| Tensile Strength at Break | <= 210 MPa | <= 30500 psi | ISO/R527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO/R527 |
| Tensile Modulus | 16.0 GPa @Temperature 23.0 °C |
2320 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Strength | <= 290 MPa | <= 42100 psi | ISO 178 |
| Flexural Modulus | 14.0 GPa @Temperature 23.0 °C |
2030 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 0.850 J/cm² @Temperature -30.0 °C |
4.04 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.20 J/cm² @Temperature -20.0 °C |
5.71 ft-lb/in² @Temperature -4.00 °F |
ISO 179 | |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | >= 200 °C @Load 5.001 kg |
>= 392 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Covestro Apec® DP9-9354T High-Heat Polycarbonate, Transparent, Flame-Retardant (discontinued **)
- LG Chemical Non-Aromatic Raffinate
- SABIC Innovative Plastics LNP LUBRICOMP DL004 PC (Europe-Africa-Middle East)
- United Cast Bar Unibar 350 Continuously Cast Iron
- Trelleborg Emerson & Cuming Eccobond® A 316 Filler End Cap Epoxy Adhesive
- Zoltek Pyron® Continuous Tow Oxidized Pan Fiber
- CMW® ELKONITE® 3W3 Tungsten Copper material ASTM B702
- Axiall 9175 White 10 Rigid PVC, Molding, White 10
- 3M 7845TL Laser Toner Printable Polyester Label Material
- BASF Elastollan S 74 D TPUR
Copyright © lookpolymers.com All Rights Reserved