- Fiberfil® PP-60/TC/10 Polypropylene Homopolymer, 10% Talc Filled
Fiberfil® PP-60/TC/10 Polypropylene Homopolymer, 10% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-60/TC/10 Polypropylene Homopolymer, 10% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.012 cm/cm @Thickness 3.17 mm |
0.012 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.014 cm/cm @Thickness 6.35 mm |
0.014 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 12 g/10 min | 12 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 - 95 | 90 - 95 | ASTM D785 |
| Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
| Elongation at Yield | 25 % | 25 % | ASTM D638 |
| Tensile Modulus | 2.34 GPa | 340 ksi | ASTM D638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D790 |
| Flexural Modulus | 2.21 GPa | 320 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Front Barrel Temperature | 182 - 199 °C | 360 - 390 °F | |
| Nozzle Temperature | 182 - 193 °C | 360 - 380 °F | |
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | |
| Mold Temperature | 32.2 - 71.1 °C | 90.0 - 160 °F | |
| Drying Temperature | 76.7 °C | 170 °F | Drying not normally required |
| Dry Time | 2 hour | 2 hour | Drying not normally required |
| Moisture Content | <= 0.20 % | <= 0.20 % | recommended for molding |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi |
Users viewing this material also viewed the following:
- LG Chemical LUPOL HG3200SK2 PP+MF20%, High Gloss
- SIDPEC EGYPTENE® HD 5301 FB HDPE Film
- Teknor Apex Sinvicomp DBS 3607 Polyvinyl Chloride, Rigid
- Daikin POLYFLON LDW-40 PTFE Low Polymer, Milky Liquid
- Dow ATTANE™ 4206 Ultra Low Density Polyethylene, Impact Modifier Grade
- Arlon 51581B015 0.015" Uncured Silicone Rubber with Fiberglass Substrate
- C.O.I.M. FILCO® 656 Unsaturated Polyester Powder Resin
- 3M Scotchcal™ ElectroCut™ 7725-77 Graphic Film
- 3M 963-10 Flexible Prismatic Conspicuity Markings
- Chesterton 635 SXC Synthetic, Extreme Pressure & Corrosion Resistant Grease
Copyright © lookpolymers.com All Rights Reserved