- Polykemi AB SCANAMID 66 A12^ F50 Nylon 66, Glass Fiber Reinforced
Polykemi AB SCANAMID 66 A12^ F50 Nylon 66, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Polykemi AB |
| Trade Name | SCANAMID 66 |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANAMID 66 A12^ F50 Nylon 66, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Filler Content | 50 % | 50 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | With Flow; ISO 2577 |
| 0.0080 cm/cm | 0.0080 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 @Time 15.0 sec |
83 @Time 0.00417 hour |
ASTM D2240 |
| Tensile Strength at Break | <= 210 MPa | <= 30500 psi | ISO/R527 |
| Elongation at Yield | 2.0 % | 2.0 % | ISO/R527 |
| Flexural Strength | <= 290 MPa | <= 42100 psi | ISO 178 |
| Flexural Modulus | 14.2 GPa @Temperature 23.0 °C |
2060 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -20.0 °C |
5.71 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | >= 230 °C @Load 5.001 kg |
>= 446 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 80 PHR Dixie Clay Filler
- Plenco 7466 Phenolic, Nodular, Injection Molded (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8135/GN PEEK, unreinforced, easy flowing
- Teknor Apex Telcar® TL-2563A Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- E-Polymers SEPAZ® V335HS 35% Glass Fiber Reinforced Heat Stabilized PPA
- Azdel Plus R300-B01 30% Continuous Random Fiber Mat / PP Resin Matrix
- Abatron 8509-3 A/B Carbon-Filled Electrically Conductive Epoxy Compound
- Ascend Performance Materials Vydyne® 49H NT Nylon 66, Impact Modified, Conditioned
Copyright © lookpolymers.com All Rights Reserved