| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | EMERGE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron EMERGEâ„¢ 4530-6 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EMERGEâ„¢ PC 4510-15 advanced resin is a general purpose polycarbonate resin offering ultraviolet light stability, ignition resistance, heat resistance and excellent toughness. Applications: Consumer Electronics and Information Technology Equipment Computer and Business Equipment Portable Electronics Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 72.4 MPa | 10500 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Elongation at Break | 150 % | 150 % | 0.125 in, injection molded, unannealed; ASTM D638 |
| Tensile Modulus | 2.30 GPa | 334 ksi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | 0.125 in, injection molded, unannealed; ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 0.125 in, injection molded, unannealed; ASTM D790 |
| Izod Impact, Notched | 9.08 J/cm | 17.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | 0.157 in, annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | 0.157 in, unannealed; ASTM D648 |
| 139 °C | 282 °F | 0.157 in, annealed; ASTM D648 | |
| Vicat Softening Point | 148 °C | 298 °F | 50°C/hr, 50N; ASTM D1525 |
| Flammability, UL94 | V-2 | V-2 | 0.0625 in |
| V-2 | V-2 | 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 299 - 327 °C | 570 - 621 °F | |
| Mold Temperature | 77.0 - 110 °C | 171 - 230 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- Covestro Petlon® DP3-1027 Semi-Crystalline PET, 45% Glass Fiber (discontinued **)
- Zircar Zirconia ZYP-55 Zirconia Powder
- Styrolution PS 153A GPPS
- Styron XZ 94462.01 Carboxylated SB
- Schmolz + Bickenbach UGIMA 303 UX® Stainless Steel Bar
- Valley Adhesives EM-422 High Temperature Application Glue Stick
- DSM Akulon® K224-PG8 (Cond.) 40% Glass Reinforced, Impact Modified Nylon 6 (North America)
- DuPont Teijin Films Melinex® FRP Polyester Film, 92 Gauge
- 3M Scotchcal™ ElectroCut™ 7725-27 Graphic Film
- Aclo Accutech Polypropylene Copolymer CP0436G10CL Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved