Polykemi AB POLYfill PPHC TS25020 Polypropylene, Mineral Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer Polykemi AB
Trade Name POLYfill
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Polykemi AB POLYfill PPHC TS25020 Polypropylene, Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Filler Content 20 %
20 %
±2%; Polykemi
Linear Mold Shrinkage 0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
With Flow; ISO 2577
0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
Across Flow; ISO 2577
Melt Index of Compound 25 g/10 min
<br>@Load 2.16 kg,<br> Temperature 230 °C
 25 g/10 min
<br>@Load 4.76 lb,<br> Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 28.0 MPa
<= 4060 psi
ISO/R527
Elongation at Yield 8.0 %
8.0 %
ISO/R527
Flexural Strength <= 45.0 MPa
<= 6530 psi
ISO 178
Flexural Modulus 1.90 GPa
<br>@Temperature 23.0 °C
 276 ksi
<br>@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.400 J/cm²
<br>@Temperature 23.0 °C
 1.90 ft-lb/in²
<br>@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
120°C/h; ISO 75/1
Vicat Softening Point 81.0 °C
<br>@Load 5.001 kg
 178 °F
<br>@Load 11.03 lb
 50°C/h; ISO 306
142 °C
<br>@Load 1.00 kg
 288 °F
<br>@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB
<br>@Thickness 1.60 mm
 HB
<br>@Thickness 0.0630 in
Glow Wire Test 750 °C
<br>@Thickness 2.00 mm
 1380 °F
<br>@Thickness 0.0787 in
 IEC 695-2-1