Lanxess Pocan® BF 8230 000000 PBT, 30% Glass Fiber

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Pocan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® BF 8230 000000 PBT, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, 30% glass spheres/glass fibers, injection molding, flame retardant, low tendency to warp, improved surface finish
Physical Properties Metric English Comments
Density 1.67 g/cc
0.0603 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 0.10 %
0.10 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 95 cm³/g
95 cm³/g
Viscosity number; ISO 307, 1157, 1628
Melt Flow 63 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 63 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 95.0 MPa
13800 psi
ISO 527-1/-2
Elongation at Yield 2.0 %
2.0 %
ISO 527-1/-2
Tensile Modulus 7.50 GPa
1090 ksi
ISO 527-1/-2
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C
16.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C
38.9 µin/in-°F
ISO 11359-1/-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 70.0 °C
158 °F
ISO 75-1/-2
Vicat Softening Point 200 °C
392 °F
50°C/h 50N; ISO 306
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 IEC 60695-11-10
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 IEC 60695-11-10
Oxygen Index 32 %
32 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+13 ohm
>= 1.00e+13 ohm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
 3.8

@Frequency 1.00e+6 Hz
 IEC 60250
4.0

@Frequency 100 Hz
 4.0

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 21.0 kV/mm
533 kV/in
IEC 60243-1
Dissipation Factor 0.013

@Frequency 100 Hz
 0.013

@Frequency 100 Hz
 IEC 60250
0.017

@Frequency 1.00e+6 Hz
 0.017

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 175 V
175 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 10724
Descriptive Properties Value Comments
Form Pellets
ISO Shortname ISO 7792-1-PBT,GFHMR,09-070,(GB+GF)30; ISO 1043-PBT (GB+GF) FR(17)
Processing Injection molding