Polykemi AB POLYfill PPH GF5030 HC Polypropylene Homopolymer, Glass Fibre-Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer Polykemi AB
Trade Name POLYfill
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Polykemi AB POLYfill PPH GF5030 HC Polypropylene Homopolymer, Glass Fibre-Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
ISO 1183
Filler Content 30 %
30 %
±2%; Polykemi
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
With Flow; ISO 2577
0.0080 cm/cm
0.0080 in/in
Across Flow; ISO 2577
Melt Index of Compound 5.0 g/10 min
<br>@Load 2.16 kg,<br> Temperature 230 °C
 5.0 g/10 min
<br>@Load 4.76 lb,<br> Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 103 MPa
<= 14900 psi
ISO/R527
Elongation at Break 4.0 %
4.0 %
ISO/R527
Elongation at Yield 3.5 %
3.5 %
ISO/R527
Flexural Strength <= 158 MPa
<= 22900 psi
ISO 178
Flexural Modulus 8.00 GPa
<br>@Temperature 23.0 °C
 1160 ksi
<br>@Temperature 73.4 °F
 ISO 178
Charpy Impact Unnotched 3.90 J/cm²
<br>@Temperature -20.0 °C
 18.6 ft-lb/in²
<br>@Temperature -4.00 °F
 ISO 179
NB
<br>@Temperature 23.0 °C
 NB
<br>@Temperature 73.4 °F
 ISO 179
Charpy Impact, Notched 0.700 J/cm²
<br>@Temperature -20.0 °C
 3.33 ft-lb/in²
<br>@Temperature -4.00 °F
 ISO 179
1.00 J/cm²
<br>@Temperature 23.0 °C
 4.76 ft-lb/in²
<br>@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 159 °C
318 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 149 °C
300 °F
120°C/h; ISO 75/1
Vicat Softening Point 143 °C
<br>@Load 5.001 kg
 289 °F
<br>@Load 11.03 lb
 50°C/h; ISO 306
166 °C
<br>@Load 1.00 kg
 331 °F
<br>@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB
<br>@Thickness 1.60 mm
 HB
<br>@Thickness 0.0630 in
Glow Wire Test 750 °C
<br>@Thickness 2.00 mm
 1380 °F
<br>@Thickness 0.0787 in
 IEC 695-2-1
Processing Properties Metric English Comments
Melt Temperature 205 - 260 °C
401 - 500 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Dry Time 2 - 4 hour
2 - 4 hour
in circulation dryer
2 - 4 hour
2 - 4 hour
in desiccant air dryer
Injection Pressure 40.0 - 110 MPa
5800 - 16000 psi
Back Pressure 1.00 - 2.00 MPa
145 - 290 psi
Descriptive Properties Value Comments
Holding Pressure () 20-40
% of injection pressure
Injection Speed () High