SABIC Innovative Plastics ULTEM CRS5011 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM CRS5011 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent, Enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 11 g/10 min @Load 6.60 kg, Temperature 337 °C |
11 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 99.0 MPa | 14400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.89 GPa | 419 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 137 MPa | 19900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| 20.82 J/cm @Thickness 3.20 mm |
39.00 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 225 °C | 437 °F | |
| UL RTI, Electrical | 160 °C | 320 °F | UL 746B |
| UL RTI, Mechanical with Impact | 155 °C | 311 °F | UL 746B |
| UL RTI, Mechanical without Impact | 160 °C | 320 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.2 @Frequency 50.0 - 60.0 Hz |
3.2 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Dielectric Strength | 17.9 kV/mm @Thickness 3.20 mm |
455 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0021 @Frequency 50.0 - 60.0 Hz |
0.0021 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Users viewing this material also viewed the following:
- Lanxess Durethan® DP BKV 240 H2.0 901510 Copolyamide, 40% Glass Fiber
- Momentive Performance Materials RTV6126 Clear Potting/Encapsulating Gel
- SABIC Innovative Plastics LNP Thermocomp MH0200A PP (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP WF006H PBT (Asia Pacific)
- Solvay JAGUAR® 418 Surfactant
- ChevronTexaco Fuel Oil 6
- ChevronTexaco RPM® SAE 30 Heavy Duty Motor Oil
- Arkema Group Appryl® 7280 Polypropylene - Polyethylene Copolymer
- Unifrax Fiberfrax® 970 Ceramic Fiber Paper
Copyright © lookpolymers.com All Rights Reserved