PolyOne Stat-Tech™ PP-16CP/000-2 HI Polypropylene, Unspecified (PP, Unspecified)

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	PolyOne Corporation
Trade Name	Stat-Tech™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Stat-Tech™ PP-16CP/000-2 HI Polypropylene, Unspecified (PP, Unspecified).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Stat-Tech™ electrically conductive compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	0.998 g/cc	0.998 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0080 - 0.010 cm/cm	0.0080 - 0.010 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm	0.0080 - 0.010 in/in	ASTM D955
Melt Flow	5.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C	5.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F	Procedure A; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	25.5 MPa	3700 psi	ASTM D638
Elongation at Break	20 %	20 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	1.99 GPa	289 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	42.4 MPa	6150 psi	ASTM D790
Flexural Modulus	1.69 GPa	245 ksi	ASTM D790
Izod Impact, Notched	3.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	5.99 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	98.0 °C @Thickness 3.18 mm	208 °F @Thickness 0.125 in	Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C @Thickness 3.18 mm	122 °F @Thickness 0.125 in	Annealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	1000 ohm-cm - 1e+05	1000 ohm-cm - 1e+05	ASTM D257
Surface Resistance	1000 ohm - 1e+05	1000 ohm - 1e+05	ASTM D257
Static Decay	0.0020 sec	0.0020 sec	(Mil-B-81705C), 12% RH, 5000 kV to 50 kV

Processing Properties	Metric	English	Comments
Melt Temperature	199 - 221 °C	390 - 430 °F

Descriptive Properties	Value	Comments
Features	Antistatic
	Conductive
	Electrically Conductive
	Statically Conductive
Filler / Reinforcement	Carbon Powder, 16% Filler by Weight
Forms	Pellets
Generic Material	PP, Unspecified
Generic Name	Polypropylene, Unspecified (PP, Unspecified)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Aerospace Applications
	Automotive Electronics
	Business Equipment
	Computer Components
	Connectors
	Electrical Housing
	Electrical/Electronic Applications
	Housings